TEST ITEMS
UNITTEST METHODSTANDARDTYPICAL VALUEAPPEARANCE
-
Naked Eye
Good
Good
SPECIFIC GRAVITY
g/Cm3
IEC 60811
1.50(±0.02)
1.50
TENSILE STRENGTH
Kgf/mm2
IEC 60811
Min 1.27
1.6~1.8
ELONGATION
%
IEC 60811
Min 150
240~270
AFTER AGING
(100oc * 168h)
Retention of T/S
%
IEC 60811
±25
90~100
Retention of longation
%
IEC 60811
±25
80~90
VOLUME RESISTIVITY at 20°C
Ω.cm
IEC 60502
1.0 x 1013
1.0 x 1013
HEAT DEFORMATION
%
IEC 60811
Max 50
20~30
OXIGEN INDEX (O/I)
%
KSM 3032
Min 30
31
HARDNESS
Shore A
ISO868
88(±3)
88
Items
C1
C2
C3
C4
Neck
X-Head
Die
Temperature (oC)
145oC
150 oC
155 oC
160 oC
165 oC
165 oC
170 oC
Note:The above temperature can be changeable depending on the real heat dissemination of plated machine