PTFE Coated Open Mesh Conveyor Belt for UV oven
PTFE coated open mesh belt select fine fiberglass, Kevlar or Nomex as basic weaving material, coated with excellent PTFE resin to make it into various of PTFE conveyor belt.
1. Outstanding temperature resistance (from -170ºC to +260ºC)
2. Resistant to corrosive agents
3. Low thermal mass
4. Controlled porosity
5. Superior non-stick surface, easy to clean
6. Dimensional stability
7.Non-toxic
PTFEopen mesh belts are used in screen printing to transport imprinted materials through drying ovens and cooling chambers. These belts are long lasting and perform well over a wode range of operating temperatures.
Fiber teflon belt fabrication department can supply a wide variety of splices and edge reinforcements in order to respond customer’s specific applications.
Item
MeshSize
material
Thickness
Weight
Temperature
resistance
MaxWidth
Tensile
Strength
6001
1x1mm
fiberglass
0.5mm
370g/m²
-70-260°C
4000mm
310/290N/cm
6002
2x2mm
fiberglass
0.7mm
450g/m²
-70-260°C
4000mm
350/310N/cm
6003
4x4mm
fiberglass
(black)
1.0mm
400g/m²
-70-260°C
4000mm
390/320N/cm
6004
4x4mm
fiberglass
1.0mm
450g/m²
-70-260°C
4000mm
390/320N/cm
6007
4x4mm
Kevlar+
fiberglass
1.2mm
600g/m²
-70-260°C
4000mm
895/370N/cm
6008
4x4mm
fiberglass
1.2mm
580g/m²
-70-260°C
4000mm
560/360N/cm
6010
4x4mm
Kevlar
1.0mm
500g/m²
-70-260°C
4000mm
900/600N/cm
6012
4x4mm
fiberglass
(black)
1.0mm
550g/m²
-70-260°C
4000mm
395/370N/cm
6013
10x10mm
fiberglass
1.0mm
450g/m²
-70-260°C
4000mm
360/300N/cm
6015
2x2.5mm
fiberglass
0.9mm
600g/m²
-70-260°C
4000mm
390/320N/cm
There are a number of factors to keep in mind when choosing the belting material for your application:
* Temperature Range – Our ptfe fabrics have the capabilities of withstanding -70°C- +260°C constant operating temperatures.
* Pliability – If the material is to track around pulleys that drive the belt, the diameter of the pulley is critical.The smaller the roller the more flexible the belt must be. Vichen’s thinner materials (0.010” and under) are more pliant than the heavier coated fabrics.
* Release Qualities – The surface finishes of our materials range from a rough, semi-porous finish to a super smooth surface. The release or fabric impression results desired will be a determining factor.
* Strength – Options to be considered are breaking, tensile and tear strength. How much of a load the belt carries, how fast it moves and how tightly it will be tensioned all must be considered.