Pvc Resin Cable Pvc Resin Cable Resin

Product DescriptionGradeUL80℃ standard cable materialUL105℃standard cable materialPropertiesUnits/
TermsEUL80-K/UL1007EUL80-K/UL1015EUL105-K/UL1015EUL105-K/UL1007
TempResistance℃8080105105
HardnessShoreA89±2A89±2A88A±2A(45P)88A±2A(45P)
TensileStrengthPSI≥2000≥1900≥1700≥1750
Elongationatbreak%≥200≥190≥180≥180
Coldbendtemp℃/4H-20-20-20-20
InsulationResistanceM•KM≥2.5≥2.5≥2.5≥10
BurningtestVW-1VW-1VW-1VW-1
Agingtemp℃113113136136
AgingtimeH168168168168
T.SAfterAgingPSI≥2200≥2000≥1900≥1950
T.Sresidualrate%≥70≥70≥75≥75
Elongationatbreakafteraging%≥160≥170≥130≥135
Elongationresidualrate%≥65≥65≥65≥65
SpecialGravityg/cm31.43±0.021.43±0.021.43±0.021.43±0.02
1.Technical specifications of 70 ℃ pvc compound
Tensilestrength
MPa
20.5
Fracturetensilestrain
%
320
Ageing temperature
℃
100
Ageing time
h
168
Tensilestrengthafterageing
MPa
22.5
Maxchangeoftensilestrength
%
+12
Afterageingfracturetensilestrain
%
290
Maxchangeof fracturetensilestrain
%
-10
Thermaldeformation
%
28
Thermalageingqualityloss
g/m2
19
200℃thermalstabilitytime
min
90
20℃volumeresistivity
Ω.cm
2.0*1011
Technical specifications of 90 ℃ pvc resin compound
Tensilestrength
MPa
20
Fracturetensilestrain
%
330
Ageing temperature
℃
100
Ageing time
h
240
Tensilestrengthafterageing
MPa
21.5
Maxchangeoftensilestrength
%
+8
Afterageingfracturetensilestrain
%
310
Maxchangeof fracturetensilestrain
%
-6
Thermaldeformation
%
28
Thermalageingqualityloss
g/m2
9
200℃thermalstabilitytime
min
120
20℃volumeresistivity
Ω.cm
2.0*1010
2,Use and standard: wire and cable
3,Process: extrusion
4,Appearance: cylindrical particles, plastication should be good, the color and luster is even, without obvious impurity.
5,color: Any colors, base on requirement.
6,Packing: 25kg net weightper in a kraft bag.
7, Transportation and storage:
This kind of product in the transportation should not be weathered, should be stored in a clean, cool, dry and ventilated warehouse , storage period is from the date for a year.
We will also producethe products according with customer's requirement, For example, Flame-resisting compounds, Low temperature resisting compounds, Heat-resistant compounds, and low smoke low halogen compounds,Transparent PVC compoundsetc.