LDPE-isusedinproductsandpackagingsuchasplasticbags,milkjugs,detergentbottles,margarinetubs,garbagecontainers,waterpipes,wovenbag,raincoat,polyethylenemonofilament,wovenyarnetc..LDPEresinsaremadebyhighpressureautoclaveprocessandmainlyusedforblownfilmextrusionandwirecoating(cablesheath)etc..Theyarewidelyusedforapplicationsforgeneralpurposepackagingfilms,heavydutybags,shrinkfilms,andfoams.
LDPE Injection Grade
Tests
Value
Unit
Melt Flow Rate (MFR)
15
g/10min
Density
0.922
g/cm3
Tensile Yield Strength
7
Mpa
Elongation at Break
75
%
Wien Softening Point
85
°C
Packing
In 25 kg PP woven bags,20MT/20’FCL
LDPE Film Grade
Tests
Value
Unit
Melt Flow Rate (MFR)
2
g/10min
Density
0.9225
g/cm3
Tensile Strength
9
Mpa
Elongation at Break
500
%
Fish eye max(0.3-2mm)
30
n/1200cm2
Stripes
20
cm/20m3
Packing
In 25 kg PP woven bags,20MT/20’FCL