Introduction of aac block production line
AAC Brick Production Line (light brick ) is the light and porous buidling material. It has light weight keeping temperature cant burn and other advantages.it can be made into many kinds of bricks(for example:600x200x100,80x80x180,240x115x53,600x200x125),they could be used industry building and common building.they are more and more popular in the world.in the future,they will replace the Clay brick completely.
AAC block Production Line
Common concrete density is usually 1600- 2400kg/m3,but AAC Machine are 550kg/m3-680kg/m3
It has not the big grain,main use silicon material (for example:coal ash,sand,stone dust and others ),through making the material small for example sand,they can be used directly if has enough degree of small (for example coal ash.Mixing calcium material lime cement water to a special slop,then add the aluminum dust and the additive.Make the aluminum dust and the special slop have a Chemical reflect.then produce Hydrogen to make the concrete slop to expanding or swell,foam.Next,put them into the curing room to concreting cutting steaming curing,last,there will bacome the light brick,the porous rate is 70-80%.
AAC block Production Line
stocking raw materials, mixing, molding, forming, cutting, evaporating and curing, crane cramp, transporting etc.,
1 Product weight is according to 600kg/m3 to control.
2 annual capacity 300,000M3.
3 set raw material proportion: cement 6.5%, raw lime 23%, flyash 68%, gypsum 3%, aluminum paste powder 350g/M3.
4 water and material rate 0.631
5 one mould product 2.88M3
6 Casting slurry cycle time 5-6 minutes, cut cycle time 5 minutes.
7 casting slurry temperature 38-42 degree
8 body quiet stop. Time is 1.5-2.5hours, temperature 50-
90 degree, after quiet stop body strength is 0.15-0.18Mpa
9 Steam curing cycle time, come in and out autoclave about 0.5hour, steam curing cycle time about is 6 hours/1.6Mpa, total 6.5 hours.
10. Cement lime fly ash style aerated block raw material proportion
name
unit
Cement lime fly ash
flash
%
65-70
cement
%
6-15
lime
%
18-25
gypsum
%
3-5
Aluminum powder paste(600kg/m3)
1/10000
8
Water & material rate
0.60-0.65
Casting system
OC
36-40
Aluminum mixing time
S
30-40
11. Cement lime Sand style aerated block raw material proportion
Name
Unit
Cement Lime Sand
Sand
%
55-65
Cement
%
10-20
Lime
%
20-30
Gypsum
%
2-3
Aluminum powder paste(600kg/m3)
1/10000
8
Water & material rate
0.65-0.75
Casting system
OC
35-38