pvc foam board production line

pvc foam board production line
A.Formula and raw material description None wood powder formulaWith wood powder formulaCPE135AImpact modifier3CPE135AImpact modifier3Foaming regulatorZB-5306Foaming regulatorZB-5306AC Foaming reagent0.4AC Foaming reagent0.4Foaming accelerator composition5Foaming accelerator composition5CN-0100.4CN-0100.4NONE Oxide wax PE0.1PVC Resin powder75PVC Resin powder75Calcium carbonate23Calcium carbonate11.5NONE Wood powder11.5Epoxy soybean oil3Epoxy soybean oil4Foamed broken material10-30Foamed broken material10-30

(1) It is suitable that the PVC resin powder has a polymerization degree of 700. Japan's S-1007, S-700, South Korea's LS-70, Shanghai chlor-alkali WS-700.
(2) Since calcium carbonate is easily damp, calcium carbonate is preferably a surface-treated light active calcium carbonate having a fineness of 800 mesh or more.
(3) The foaming accelerator composition contains a stabilizer and a foaming accelerator, and CN-010 is a heat-dissipating and blowing foaming agent, and it is necessary to use HYPET products.
(4) Adding about 30 pieces of crushed material is beneficial to the stability of the feed without affecting the foaming effect.
(5) AC foaming agent and CN-010 should pay special attention to moisture.
All other raw materials should be checked for moisture and precautions should be taken. After the materials are finished, the bags should be sealed in time to avoid moisture.
The production processing of PVC skin foam board is as follows:
PVC resin + additive → high speed mixing → low speed cold mixing → cone twin screw extrusion → die shaping (crust foaming) → cooling setting → multi-roller traction → cutting products → collection inspection
Main technical parameters of PVC crust foam board production line TypeWidthThickness ExtruderOutput Motor Semi-skin foam board 1220-1600mm5-22mmSJZ80/156400Kg/h90kw Co-extruder foam board1220-1600mm3-22mm SJZ65/132 or SJZ80/156350-450kg/h50kw/90kw
Company Information

1. We have more than 30 years in extrusion field
2. Introduction from German tech and experience for the design and making twin screw extruders. And leaded by Germany experts Mr. Youcef and Mr. Elben for the long time
3. Designed and produced twin conical screw extruder, twin parallel screw extruder, and transfer the technology to the biggest gears factory in India
4. With high professional design team
5. A base combined with designing, making, studying in extrusion industrial.
6. Our philosophy is to learn advanced technology, make the best suitable machine, best efficient machine and best lines.
Factory
State of art design, process and expeirience for parallel and conic twin screw extruder gear box
Suitable design for differnce material, based on vast practical experience
Hypet has set up Separate laboratory with top equipments
Extrusion performances and capacity are proved by trail commissioning
Capalbe of providing tailer made solution for customers
Capable of providing on site technical training
Unique design , same line, differnce products
Also provide various down stream and auxiliary machines for pipe, profile and wpc
History
1. In 2002 the company was established.
2. In 2004, the establishment of plastic extrusion machinery Institute to study and study the German extrusion machinery technology.
3. In 2006, developed a continuous straight cone double reducer, for the Chinese machinery to jump on a step to contribute.
4. In 2007, developed a series of flat double reducer, the smallest 65, the largest 130, to fill the gaps in the domestic, while forming a high level of flat and cone series twin screw extruder, welcomed by the market warmly.
5. In 2008, the opening of its own 10,000 square meters of large-scale mechanical plant, as Huiyi large-scale production base.
6. In 2009, developed its own twin-screw split double alloy barrel, wear-resistant, long life, has been well received by customers, and some customers can even use 7 years.
7. In 2010, focusing on the development of Pakistan, India, Kenya, Algeria, Egypt, Saudi Arabia, Brazil, the United States, Portugal and other countries of the customer network.
8. In 2012 PE / PRR pipe unit R & D success, the most advanced and efficient single screw extruder, to achieve high yield, high efficiency, low energy consumption of the best results, screw barrel bimetallic, life than the general to extend 80%.
9. In 2013, flat double extruder on the steps, PS67 / 27 parallel twin extruder 30kW motor production reached 300 kg / h 90/27 to 500kg / h, PS107 / 27 extruder to 800kg / h.
10. In 2014, cone double extruder power unchanged, yield increased by 30%, ZS65 / 132 extruder production reached 350kg / h, ZS80 / 156 extruder production reached 550kg / h
11. In 2014 sales of flat double reducer technology to India.
12. In 2015, with foreign experts to develop suitable for plastic machinery energy-saving devices, energy saving up to 25-30%, is currently applying for technical patents.
13. In 2016, the development of a new technology 630PVC large tube unit, high output, stable and reliable production, to the advanced level.