Galvanized used stainless steel wire rope 6X29FIPFC

ITEMS
Unit
930dtex1
(840D/1)
1400dtex1
(1260D/1)
1870dtex1
(1680D/1)
1
Breaking strength
N/end
≥70
≥105
≥127
2
Elongation at 44.1N
%
8±1.0
3
Elongation at 33.3N
%
7.5±1.0
4
Elongation at 22.6N
%
7.5±1.0
5
Adhesive strength
N/end
≥49
≥64
≥78
6
Diameter
MM
0.32±0.03
0.43±0.03
0.50±0.03
7
Twist
T/ 10cm
21±1.5
19±1.5
19±1.5
8
Unevenness of breaking strength≤
%
≤4.5
≤4.5
≤4.5
9
Unevenness of breaking elongation≤
%
≤6.0
≤6.0
≤6.0
10
Dip pick-up
%
4.2±1.2
4.2±1.2
4.2±1.2
11
Breaking elongation
%
20±2
20±2
20±2
12
Percentage of moisture
≤
≤0.8
≤0.8
≤0.8
13
Dry-hot shrinkage
≤
≤4.0
≤4.0
≤4.0ITEMS
UNITE
840D/1
840D/2
1260D/2
1260D/3
1680D/2
1890D/2
930
dtex/1
930
dtex/2
1400
dtex/2
1400
dtex/3
1870
dtex/2
2100
dtex/2
1
Breaking Stength (min)
N/end ≥
67
132
205
305
270
305
2
Elongation
at 22.1 N
%
7.0 ± 1.0
Elongation
at 44.1 N
%
8.0 ± 1.0
Elongation
at 66.6 N
%
8.5 ± 1.0
Elongation
at 88.2 N
%
8.5 ± 1.0
Elongation
at 100 N
%
9.0 ± 1.0
9.0 ± 1.0
3
Adhesion (H-test) (min)
N/Cm ≥
49
98
117
150
137
150
4
Breaking strength difference (max)
≤ %
4
4
4
4
4
4
5
Breaking elongation difference (max)
≤ %
6
6
6
6
6
6
6
Dip pick up
%
5.0 ± 1.2
4.5 ± 1
4.5 ± 1
4.5 ± 1
4.5 ± 1
4.5 ± 1
7
Breaking elongation
%
20 ± 2
22 ± 2
23 ± 2
23 ± 2
23 ± 2
23 ± 2
8
Diameter
mm
0.32 ± 0.03
0.55 ± 0.04
0.65 ± 0.04
0.78 ± 0.04
0.75 ± 0.04
0.78 ± 0.04
9
Twist Single twist (Z)
T/ 10cm
21 ± 1.5
46 ± 1.5
38 ± 1.5
32 ± 1.5
33 ± 1.5
32 ± 1.5
Ply twist (S)
/
46 ± 1.5
38 ± 1.5
32 ± 1.5
33 ± 1.5
32 ± 1.5
10
Hot air shrinkage
150 °C x30min(max)
≤ %
6.0
7.0
7.0
7.0
7.0
7.0